Method for forming dielectric film of capacitor

ABSTRACT

A method for forming a dielectric film of a capacitor includes injecting a first source containing a first component into a reaction chamber to be adsorbed on a surface of a substrate, purging residual first source out of the reaction chamber, injecting a mixed gas of Ar and O 2  in plasma state into the reaction chamber to react with the first component adsorbed on the substrate, purging by-products and residual gas out of the reaction chamber, injecting a second source containing a second component into the reaction chamber to be adsorbed to the surface of the resulting structure, purging residual second source out of the reaction chamber, injecting a mixed gas of Ar and O 2  in plasma state into the reaction chamber to induce oxidation reaction and purging residual gas and by-products out of the reaction chamber using mixed gas of Ar and O 2  for obtaining sufficient capacitance for highly integrated semiconductor devices.

BACKGROUND

[0001] 1. Technical Field

[0002] Methods for forming dielectric films of capacitors are disclosed wherein a high K oxide monoatomic layer having a high dielectric constant such as SrTiO₃ and (Ba,Sr)TiO₃ is formed by using an atomic layer deposition having high step coverage to provide sufficient capacitance for high integration of the semiconductor device in case of a capacitor having a high aspect ratio and a geometrically-complicated structure.

[0003] 2. Description of the Related Art

[0004] As the size of a cell decreases due to high integration density, it becomes more difficult to obtain sufficient capacitance which is proportional to the surface area of a storage node.

[0005] In particular, in the DRAM wherein a unit cell includes a MOS transistor and a capacitor, a capacitance of the capacitor needs to be increased and an area occupied by the capacitor needs to be decreased to achieve high integration.

[0006] Therefore, in order to increase the capacitance of the capacitor which follows the equation (Eo×Er×A)/T (where Eo denotes a vacuum dielectric constant, Er denotes a dielectric constant of a dielectric film, A denotes an area of the capacitor and T denotes a thickness of the dielectric film), a method of increasing a surface area of a storage node which is a lower electrode has been proposed.

[0007] However, the method for increasing the surface area of the storage node has reached a limit due to the high integration density and process limitations of the semiconductor device.

[0008] Recently, a method for forming a capacitor using a dielectric film having a high dielectric constant has been proposed to obtain sufficient capacitance for highly integrated semiconductor devices.

[0009] The dielectric film having a high dielectric constant is deposited on the surface of the storage node having a large step difference according to atomic layer deposition. However, when atomic layer deposition is performed to form a dielectric layer from at least two source materials, the composition of the dielectric layer becomes very difficult to control.

[0010] A method for controlling the composition of dielectric layers by varying a feed ratio of each source material has been suggested. However, precise control of the feed ratio is almost impossible since the feed ratio is a multiple of the intrinsic deposition rate of each source material.

[0011]FIG. 1 is a graph showing a conventional method for controlling the composition of a dielectric layer formed from two source materials and a reaction gas using atomic layer deposition, wherein general variations in the deposition rate relative to the flow rate of the reaction gas is illustrated.

[0012] Since the atomic layer deposition is based on adsorption reaction on the surface of a substrate, the deposition rate saturates to a predetermined value when flow rate of the reaction gas reaches a predetermined value.

[0013] Here, a and b of FIG. 1 which are the deposition rates at saturation have specific values according to each source material and reaction gas.

[0014] In addition, when chemical properties of the source materials and the reaction gas are determined, critical values of the source gas and the reaction gas are fixed to one value to obtain the saturated deposition rate a or b.

[0015] Accordingly, when the oxide thin film composed of a material having at least two components is formed according to the atomic layer deposition, a complicated process results wherein the feeding ratio of each source is varied as required to form the oxide thin film having stoichiometric compositions with the saturated deposition rate.

SUMMARY OF THE DISCLOSURE

[0016] Accordingly, a method for forming a dielectric film of a capacitor is disclosed which has sufficient capacitance for highly integrated semiconductor devices by forming a dielectric film having a high dielectric constant using atomic layer deposition with excellent step coverage.

[0017] One disclosed method for forming a multi-component dielectric film comprises: (a) injecting a first source containing a first component into a reaction chamber to be adsorbed on a surface of a substrate; (b) purging residual first source out of the reaction chamber; (c) injecting a mixed gas of Ar and O₂ in plasma state into the reaction chamber to react with the first component adsorbed on the substrate; (d) purging by-products and residual gas out of the reaction chamber; (e) injecting a second source containing a second component into the reaction chamber to be adsorbed to the surface of the resulting structure; (f) purging residual second source out of the reaction chamber; (g) injecting a mixed gas of Ar and O₂ in plasma state into the reaction chamber to induce oxidation reaction; and (h) purging residual gas and by-products out of the reaction chamber using mixed gas of Ar and O₂, wherein the substrate is selected from the group consisting of Si, SiO₂, TiN, TiSiN, TiAlN, Ru, Pt, Ir, RuO₂, IrO₂, and combinations thereof; the purge processes of step (b), (d), (f) and (h) are performed using a vacuum pump; the purge processes of step (b), (d), (f) and (h) are performed using a vacuum pump with an inert gas added thereto; the method further comprises a step of injecting O₂ gas into the reaction chamber for 0.1 to 10 seconds during the step (c) and (g), respectively; step (c) and (g) is performed on the condition of maintaining the reaction chamber at a pressure ranges from 0.5 to 5.0 Torr; the O₂ gas ratio of the mixed gas of Ar and O₂ in plasma state is 20 to 40% in the step (c) and (g), respectively; mixed gas of Ar and O₂ in plasma state is generated in the reaction chamber or a remotely generated out of the chamber and then supplied into the reaction chamber; during the step (a) to (h) the substrate is maintained at a temperature ranging from 150 to 300° C. and the first source and the second source are injected for a time period ranging from 0.1 to 10 seconds; one of the first source and the second source is Sr and the other is Ti; the Sr source is selected from the group consisting of Sr(THD)₂, Sr(METHD)₂, and solutions thereof; the Ti source is selected from the group consisting of Ti(i-OC₃H₇)₄, Ti(n-OC₄H₉)₄, Ti(t-OC₄H₇)₄, Ti(OC₂H₅)₄, Ti(OCH₃)₄, Ti(n-OC₃H₇)₄ and combinations thereof; the Sr source and the Ti source are injected for a time period ranging from 0.1 to 10 seconds in the processes (a) and (e), respectively; the purge processes of step (b), (d), (f) and (h) are performed using a vacuum pump; the purge processes of step (b), (d), (f) and (h) are performed using a vacuum pump with an inert gas added thereto; the step (c) and (g) is performed on the condition of: maintaining the pressure of the reaction chamber ranging from 0.5 to 5.0 Torr; injecting O₂ for a time period ranging from 0.1 to 10 seconds; and injecting a mixed gas of Ar and O₂; the mixed gas of Ar and O₂ in plasma state is generated in the reaction chamber or a remotely generated and then supplied into the reaction chamber; the O₂ gas ratio of the mixed gas of Ar and O₂ in plasma state is 20 to 40%; the substrate is maintained at a temperature ranging from 150 to 300° C. and the first source and the second source are injected for a time period ranging from 0.1 to 10 seconds in the step (a) to (h), respectively; and the first source is a cocktail source of Sr/Ti and the second source is Ti source.

[0018] The principles of the disclosed methods will now be explained.

[0019] The disclosed method controls compositions of dielectric layers by using differences of reaction rates between reaction gas and each source material while using conventional atomic layer deposition having a surface chemical reaction property of a monoatomic layer.

[0020] For example, when SrTiO thin film is formed according to atomic layer deposition using Sr source and Ti source, Ar/O₂ mixed gas is activated in a remote plasma device and injected into a reaction chamber as an oxidation source, which allow precise control of compositions of SrTiO₃ thin film without changing a feeding ratio of Si source and Ti source which are absorbed by using oxidation reaction differences between each source and Ar/O₂.

[0021] Here, Sr source is selected from the group consisting of β-Diketonate group Ligand containing Sr(THD)₂ or Sr(METHD)₂, solutions thereof, and Ti source is an alkoxide group material selected from the group consisting of Ti(i-OC₃H₇)₄, Ti(n-OC₄H₉)₄, Ti(t-OC₄H₇)₄, Ti(OC₂H₅)₄, Ti(OCH₃)₄, Ti(n-OC₃H₇)₄ and combinations thereof.

BRIEF DESCRIPTION OF THE DRAWINGS

[0022] The disclosed techniques will become better understood with reference to the accompanying drawings which are given only by way of illustration. In the drawings:

[0023]FIG. 1 is a graph showing a conventional method for controlling compositions of ternary compounds according to atomic layer deposition;

[0024]FIG. 2 is a graph showing a deposition rate according to Ar/O₂ ratio in atomic layer deposition of SrTiO₃; and

[0025]FIG. 3 is a graph showing a process for forming SrTiO₃ thin film having a high dielectric constant in accordance with the disclosed method.

DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EMBODIMENTS

[0026] A method for forming a dielectric film of capacitor in accordance with a preferred embodiment will now be described in detail with reference to the accompanying drawings.

[0027]FIG. 2 is a graph showing a deposition rate according to Ar/0 ₂ ratio in atomic layer deposition of SrTiO₃. When ratio of O₂ is increased, the deposition rate increases and saturates to a predetermined value. Here, deposition rates of TiO₂ and SrO varies greatly according to the ratio of O₂.

[0028] As shown in FIG. 2, O₂ reacts with adsorbed Ti source and thus the deposition rate reaches a saturation value when ratio of O₂ is over 10% in the case of TiO₂, while the deposition rate is gradually increased to a predetermined value when ratio of O₂ is over 20% in the case of SrO.

[0029] That is, the deposition rate of TiO₂ is an almost constant value when ratio of O₂ is 20 to 40%, while the deposition rate of SrO shows gradual increase.

[0030] The difference in deposition rate between TiO₂ and SrO shows that Sr/Ti compositions can be precisely controlled by adjusting O₂ ratio for oxidation of adsorbed Sr and Ti between 20 and 40%.

[0031]FIG. 3 is a graph showing the method for forming the capacitor of the semiconductor device in accordance with the disclosed methods, wherein one cycle of atomic layer deposition for forming SrTiO₃ thin film is shown.

[0032] Step 1:

[0033] As depicted in FIG. 3, Sr (or Ti) source is injected into a reaction chamber to induce surface adsorption reaction of the source material to a substrate.

[0034] Preferably, Sr source is Sr(THD)₂ or Sr(METHD)₂ which contains β-Diketonate family Ligand, and Ti source is Ti(OiPr)₄ of alkoxide group, Ti(i-OC₃H₇)₄, Ti(n-OC₄H₉)₄, Ti(t-OC₄H₇)₄, Ti(OC₂H₅)₄, Ti(OCH₃)₄, Ti(n-OC₃H₇)₄ or combinations thereof.

[0035] In the same manner, sources containing β-Diketonate family Ligand may be used as Sr sources, and sources of alkoxide group may be used as Ti sources.

[0036] In addition, the substrate is preferably selected from the group consisting of Si, SiO₂, TiN, TiSiN, TiAIN, Ru, Pt, Ir, RuO₂, IrO₂, and combinations thereof.

[0037] Step 2:

[0038] The residual source gas is purged out of the reaction chamber using Ar or N₂. Here, the purge process is preferably performed using a vacuum pump. An inert gas can be added thereto.

[0039] Step 3:

[0040] Ar/O₂ plasma gas having a predetermined Ar/O₂ ratio for controlling Sr/Ti compositions is injected into the reaction chamber so that the injected Ar/O₂ gas reacts with the Sr (or Ti) source absorbed to the substrate to form SrO or Ar/O₂ monoatomic layer. Here, the reaction chamber is preferably maintained at a pressure of 0.5 to 5.0 Torr, and O₂ gas may be supplied into the chamber for 0.1 to 10 seconds during the injection of Ar/0 ₂ plasma gas.

[0041] In addition, Ar/O₂ plasma gas may be generated in the reaction chamber or remotely generated and supplied into the reaction chamber.

[0042] Step 4:

[0043] The Reaction by-products generated from the oxidation reaction and residual Ar/O₂ plasma gas are purged out of the reaction chamber. Here, the purge process is preferably performed using a vacuum pump. An inert gas can be added thereto.

[0044] Step 5:

[0045] Ti source, or Sr source when Ti source is used in step 1, is supplied to the reaction chamber to induce adsorption reaction.

[0046] Step 6:

[0047] The residual gas is purged out of the reaction chamber. Here, the purge process is preferably performed using a vacuum pump. An inert gas can be added thereto.

[0048] Step 7:

[0049] Ar/O₂ plasma gas activated preferably in a remote plasma device having a predetermined Ar/O₂ ratio for oxidation reaction is injected into the reaction chamber, and the reaction chamber is maintained preferably at a pressure ranging from 0.5 to 5.0 Torr, thereby inducing the oxidation reaction. Here, when plasma type Ar/O₂ mixed gas is put into the reaction chamber, O₂ can be supplied for 0.1 to 10 seconds. Preferably, the Ar/O₂ plasma gas is a plasma generated in the reaction chamber or a remotely generated plasma to be supplied to the reaction chamber.

[0050] Step 8:

[0051] The residual gas and reaction by-products are purged out of the reaction chamber using Ar/O₂. Here, the purge process is preferably performed using a vacuum pump. An inert gas can be added thereto.

[0052] Preferably, the substrate may be maintained at a temperature ranging from 150 to 300° C. and Ti source and Sr source may be supplied for a time period ranging from 0.1 to 10 seconds during the step 1 to step 8.

[0053] One SrTiO₃ layer can be formed by performing the step 1 to step 8, and SrTiO₃ layer having a desired thickness can be formed by repeating these steps.

[0054] Ratio of Sr to Ti in the SrTiO₃ layer formed on the substrate is equal to the ratio of the deposition rate of TiO₂ to the deposition rate of SrO corresponding to a specific Ar/O₂ ratio, i.e. when ratio of Ar to O₂ is F_(O2), the ratio of Sr to Ti is R_(SrO)/R_(TiO2) as shown in FIG. 2. Thus, ratio of Sr to Ti can be precisely controlled without varing the injection rate of Sr and Ti sources according to the method of the present invention.

[0055] Here, the property of the atomic layer deposition of SrTiO₃ film is improved when the difference of the reaction characteristics to Ar/O₂ plasma between source gases is larger.

[0056] In another embodiment, BST thin film such as (Ba,Sr)TiO₃ can be formed by using Sr/Ti cocktail source instead of using Sr source.

[0057] As discussed earlier, in the disclosed methods for forming capacitors, the compositions of an oxide film having at least two components can be precisely controlled to form the high dielectric constant oxide film according to the atomic layer deposition, thereby obtaining sufficient capacitance for the high integration of the semiconductor device.

[0058] As the disclosed techniques may be embodied in several forms without departing from the spirit or essential characteristics thereof, it should also be understood that the above-described embodiments are not limited by any of the details of the foregoing description, unless otherwise specified, but rather should be construed broadly within its spirit and scope as defined in the appended claims, and therefore all changes and modifications that fall within the metes and bounds of the claims, or equivalences of such metes and bounds are therefore intended to be embraced by the appended claims. 

What is claimed is:
 1. A method for forming a multi-component dielectric film for a capacitor comprising: (a) injecting a first source containing a first component into a reaction chamber to be adsorbed on a surface of a substrate; (b) purging residual first source out of the reaction chamber; (c) injecting a mixed gas of Ar and O₂ in plasma state into the reaction chamber to react with the first component adsorbed on the substrate; (d) purging by-products and residual gas out of the reaction chamber; (e) injecting a second source containing a second component into the reaction chamber to be adsorbed to the surface of the resulting structure; (f) purging residual second source out of the reaction chamber; (g) injecting a mixed gas of Ar and O₂ in plasma state into the reaction chamber to induce oxidation reaction; and (h) purging residual gas and by-products out of the reaction chamber using mixed gas of Ar and O₂.
 2. The method according to claim 1, wherein the substrate is selected from the group consisting of Si, SiO₂, TiN, TiSiN, TiAlN, Ru, Pt, Ir, RuO₂, IrO₂, and combinations thereof.
 3. The method according to claim 1, wherein the purge processes of step (b), (d), (f) and (h) are performed using a vacuum pump.
 4. The method according to claim 1, wherein the purge processes of step (b), (d), (f) and (h) are performed using a vacuum pump with an inert gas added thereto.
 5. The method according to claim 1, further comprising a step of injecting O₂ gas into the reaction chamber for a time period ranging from 0.1 to 10 seconds during the step (c) and (g), respectively.
 6. The method according to claim 1, wherein step (c) and (g) is performed on the condition of maintaining the reaction chamber at a pressure ranges from 0.5 to 5.0 Torr.
 7. The method according to claim 1, wherein the O₂ gas ratio of the mixed gas of Ar and O₂ in plasma state is 20 to 40% in the step (c) and (g), respectively.
 8. The method according to claim 1, wherein mixed gas of Ar and O₂ in plasma state is generated in the reaction chamber or a remotely generated out of the chamber and then supplied into the reaction chamber.
 9. The method according to claim 1, wherein during the step (a) to (h) the substrate is maintained at a temperature ranging from 150 to 300° C. and the first source and the second source are injected for a time period ranging from 0.1 to 10 seconds.
 10. The method according to claim 1, wherein one of the first source and the second source is Sr and the other is Ti.
 11. The method according to claim 10, wherein the Sr source is selected from the group consisting of Sr(THD)₂, Sr(METHD)₂, and solutions thereof.
 12. The method according to claim 10, wherein the Ti source is selected from the group consisting of Ti(i-OC₃H₇)₄, Ti(n-OC₄H₉)₄, Ti(t-OC₄H₇)₄, Ti(OC₂H₅)₄, Ti(OCH₃)₄, Ti(n-OC₃H₇)₄ and combinations thereof.
 13. The method according to claim 10, wherein the Sr source and the Ti source are injected for a time period ranging from 0.1 to 10 seconds in the processes (a) and (e), respectively.
 14. The method according to claim 10, wherein the purge processes of step (b), (d), (f) and (h) are performed using a vacuum pump.
 15. The method according to claim 10, wherein the purge processes of step (b), (d), (f) and (h) are performed using a vacuum pump with an inert gas added thereto.
 16. The method according to claim 10, wherein the step (c) and (g) is performed on the condition of: maintaining the pressure of the reaction chamber ranging from 0.5 to 5.0 Torr; injecting O₂ for a time period ranging from 0.1 to 10 seconds; and injecting a mixed gas of Ar and O₂.
 17. The method according to claim 10, wherein the mixed gas of Ar and O₂ in plasma state is generated in the reaction chamber or a remotely generated and then supplied into the reaction chamber.
 18. The method according to claim 10, wherein the O₂ gas ratio of the mixed gas of Ar and O₂ in plasma state is 20 to 40%.
 19. The method according to claim 10, wherein the substrate is maintained at a temperature ranging from 150 to 300° C. and the first source and the second source are injected for a time period ranging from 0.1 to 10 seconds in the step (a) to (h), respectively.
 20. The method according to claim 1, wherein the first source is a cocktail source of Sr/Ti and the second source is Ti source. 